Mechanical & wear testing

Zwick Z050

Load cell: 50 kN
Max. rate of traverse: 0.001 mm/min - 500 mm/min
Strain measurement with videoXtens 1-120
Compression test of DIN samples down to a diameter of 2 mm
Tensile test of samples with DIN geometry A,B,E
Compression test with heating plates under air condition up to 400 °C

Instron 5969

Available load cells: 1 kN, 10 kN und 50 kN
Axial stiffness of frame: 180 kN/mm
Max. distance of traverse: 1140 mm
Max. rate of traverse: 0.001 mm/min - 600 mm/min
Strain measurement with AVE2 from Instron Accuracy class 0.5
Tensile test of samples with DIN geometry A,B,E
Compression test of DIN samples down to a diameter of 4 mm

Zwick Z005

Load cell: 10N , 200N 2,5kN
Max. rate of traverse: 0.0005 mm/min - 3000 mm/min
Strain measurement with makroXtens
3 point-bending up to 100N
Tensile test of samples with DIN geometry A,B,E

Bose ElectroForce 3510

Max. load 7.5 kN: (5.3 kN RMS), 49 Nm torsion
Cyclic test in tensile, compression and 3 point bend possible
Cyclic test with a frequency of 0.00001 Hz – 100 Hz
Linear rate 0.025 μm/s – 1.5 m/s
Max. deflection 5 mm,
Max distance of traverse 0-1000 mm

Nanovea Tribometer T50 ( Pin & disc)

Wear test:
- Pin (sample)-disc ( steal- or SiC-plate)
- Ball (WC)- disc (sample)
Variable load 1 N, 2 N, 5 N, 10 N, 20 N
Wear pattern: spiral, circular, linear
Rotation speed 0.01 to 2000 rpm
Temperature of furnace until 600 °C
Max. traveling distance of radius: 46 mm

Pendulum impact testers Zwick HIT 450P

Charpy impact test on metallic materials according to DIN EN ISO 148-1, 01/2011
Pendulum rod with head 300 J
Fin 2 mm according to ISO 148-1